在加工行業及手板打樣中，噴砂是一件非常常用的表面處理工藝，其實很多人都不知道該如何選擇手板表面處理中噴砂。所以接下來由濟南手板廠家為大家進行簡單地介紹。

In the processing industry and hand plate proofing, sandblasting is a very common surface treatment process. In fact, many people do not know how to choose sandblasting in hand plate surface treatment. So let's have a brief introduction from Jinan Handboard Factory.

噴砂加工范圍：五金除銹、鋁合金噴砂、玻璃噴砂（霧面效果）、塑膠噴砂（去毛邊）、亞克力噴砂（霧面效果）、PC、PS表面處理、樹脂表面處理、鑄造工件噴砂、鋅合金噴砂（粗糙面）、不銹鋼材料噴砂、石材料噴砂、五金除油漆、五金件除焊疤、拋丸、等配件表面處理。

Sand blasting processing scope: metal rust removal, aluminum alloy sand blasting, glass sand blasting (fog surface effect), plastic sand blasting (deburring), acrylic sand blasting (fog surface effect), PC, PS surface treatment, resin surface treatment, casting workpiece sand blasting, zinc alloy sand blasting (rough surface), stainless steel material sand blasting, stone material sand blasting, metal paint removal, metal parts welding scar removal, shot blasting, and other accessories surface treatment.

亞克力噴砂：如果客戶要求很霧，一般噴玻璃砂，如果要求高一點可以選用白剛玉。如果要求不是很霧有一定透明性就須選用玻璃珠，有時候會玻璃珠里加一點玻璃砂，這樣噴出來的效果就是是有一點點透的。

Acrylic sand blasting: if the customer requires fog, glass sand is generally sprayed. If the requirement is higher, white corundum can be used. If it is not required to be foggy and transparent, glass beads must be selected. Sometimes a little glass sand will be added to the glass beads, so that the effect of spraying is a little transparent.

不銹鋼噴砂：一般需要了解不銹鋼是什么樣的面板，有拋光面合金鋼丸，拉絲面什么是合金鋼，還有原板的霧面，需要粗糙度的，對表面平滑度沒有要求的，可以選用棕剛玉和白剛玉，有特殊要求，需要光滑的，選用玻璃珠和玻璃砂。

Stainless steel sandblasting: generally, you need to know what kind of stainless steel is, including polished surface alloy steel shot, brushed surface alloy steel, and fog surface of the original plate. If roughness is required, but there is no requirement for surface smoothness, you can choose brown corundum and white corundum. If there are special requirements and need to be smooth, you can choose glass beads and glass sand.

壓鑄件：一般都是是去除毛刺低合金鋼，一般都可以使用拋丸機低合金鋼什么是合金鋼，使用鑄鋼丸鋼珠，使用鋼珠鋼丸噴砂拋丸物體表面擦傷少，刮痕淺和小，對于去除表面污物多厚的選用鋼砂，一般可考慮鋼珠和鋼砂混合使用。如果想使得噴砂的鋁件顏色更白一些高合金鋼什么是合金鋼，應該考慮使用成本高的不銹鋼丸、鋼絲切丸，如果想節省成本，考慮鑄鋼珠和不休鋼丸按8：2的比例混合使用，噴砂拋丸時每工作一次便將鋼珠清洗一次，多噴砂拋丸幾次也可達到比較白的效果。

Die castings: generally, it is low alloy steel with burr removal. Generally, shot blasting machine can be used to remove low alloy steel. What is alloy steel? Cast steel shot and steel ball can be used. The surface of shot blasting object with steel ball and steel shot is less scratched, and the scratch is shallow and small. For removal of thick surface dirt, steel sand can be selected. Generally, the mixed use of steel ball and steel sand can be considered. If you want to make the aluminum parts sandblasted whiter, what is alloy steel, you should consider using stainless steel shot and steel wire cut shot with high cost. If you want to save costs, you should consider using cast steel ball and continuous steel shot in the ratio of 8:2. When sandblasting, the steel ball will be cleaned once every time you work, and more sandblasting can also achieve a whiter effect.

以上內容便是手板表面處理中噴砂的選用，希望能夠對大家有所幫助。如果想要了解更多關于手板的相關內容，我們將竭誠為大家服務http://www.debangboya.com。

The above content is about the selection of sandblasting in the surface treatment of the hand board. I hope it can help you. If you want to know more about the hand board, we will serve you wholeheartedly http://www.debangboya.com 。